Kimya PEKK Carbon 3D Printing filament 1.75mm 500gms
£387.00 £464.40 inc. VAT £348.30 £417.96 inc. VAT
Kimya™PEKK Carbon™3D filament belongs to the polyaryletherketone family. Polyetherketoneketone (PEKK) is a thermoplastic polymer reinforced with carbon fiber. Compared to PEEK, PEKK Carbon offers slower crystallisation speed enabling transformation at lower room temperatures. It enables parts to be created with improved visual finish and better mechanical properties.
- Description
- What is PEEK/PEKK?
- Additional information
- Reviews (0)
Description
The Kimya PEKK Carbon 3D filament belongs to the polyaryletherketone family. Polyetherketoneketone (PEKK) is a thermoplastic polymer reinforced with carbon fibre. This combination gives it a high level of rigidity and heat-resistance. It can be used as a material in components exposed to acids and hydrocarbons, such as fuel and lubricants, and also to produce components located in engine housings. The Kimya PEKK Carbon 3D filament has the following properties:
- Temperature resistance
- Reinforced with carbon fibre
- Complies with the REACH standard
2-year ARMOR warranty.
(PEKK) is a material derived from semi-cristalline thermoplastics, the polyaryletherketones (PAEKs). It is a family of materials that offers excellent thermomechanical properties and also includes PEEK, the material from the family currently most widely used.
PAEK is composed of ether and ketone; their ratio and functions influence the polymers glass transition and fusion temperature, thereby affecting their thermal resistance and blocking temperature. It is a material that offers numerous advantages such as its high level of rigidity; it is frequently compared to aluminium, although it is 40% lighter. It also offers a high level of resistance to UV and high temperatures, in addition to good chemical and abrasion resistance. However, it is expensive and difficult to transform. Additionally, few 3D printers are able to use the filament, further restricting its possibilities. Its rough surface and limited colours (black, blue, beige and green) are also drawbacks for PAEK.
FILAMENT PROPERTIES
PROPERTIES | TEST METHODS | VALUES |
---|---|---|
Diameter | INS-6712 | 1.75 ° 0.1 mm 2.85 ° 0.1 mm |
Density | ISO 1183-1 | 1.27 g/cm3 |
Moisture rate | INS-6711 | < 1 % |
Glass transition temperature (Tg) | ISO 11357-1 DSC (10°C/min – 20-410°C) | 160 °C |
PRINT PARAMETERS AND SPECIMENS DIMENSIONS
PRINTING DIRECTION | XY |
---|---|
Printing Speed | 20-40 mm/s |
Infill | 100% – rectilinear |
Infill Angle | 45°/-45° |
Nozzle Temperature | 350-390°C |
Bed T° | 110-150°C |
PRINTED SPECIMENS PROPERTIES
PROPERTIES | TEST METHODS | VALUES | |
---|---|---|---|
THERMAL PROPERTIES | Maximum use T° | – | 150 °C |
ELECTRICAL PROPERTIES | Dielectric strength | IEC 60243-1 (100°m) | 84 KV/mm |
Surface resistivity | ASTM D257 | 1016 Ohms/m° | |
MECHANICAL PROPERTIES | Tensile modulus | ISO 527 | 2,900 MPa |
Tensile Strength | ISO 527 | 39.1 MPa | |
Tensile strain at break | ISO 527 | 3 % | |
Flexural modulus | ISO 178 | 2,924 MPa | |
Flexural strength* | ISO 178 | 85.9 % | |
Charpy impact resistance | ISO 179-1/1eA | 5 kJ/m° |
Note 1 | *According to ISO 178, end of the test at 5% deformation even if there is no specimen break. |
Note 2 | The data should be considered as indicative values – Properties can be influenced by production conditions. |
PRINT SETTINGS:
- PRINT SPEED : 20-40 mm/s
- EXTRUSION TEMPERATURE : 350-390°C
- PLATFORM TEMPERATURE : 110-150°C
MISCELLANEOUS
Spool Material | PC |
Steaming Temperature | 120°C |
Steaming Duration | 4h-6h |
Find more information about our Kimya PEKK Carbon 3D filament:
- our article on the K-blog: Focus PEKK Carbon material
- our client case : AERFAST
- our client case study: CEA Saclay
Additional information
Weight | 0.5 kg |
---|---|
Filament Brand | Kimya |
Filament Colour | Black |
Filament Diameter | 1.75mm |
Filament Type | PEEK |
Filament Weight | 500gms |
Filament Weight | 500gms |
Filament Range | Kimya PEKK |